可靠性数据 |
|
试验 |
实验方法 |
CCH |
CCE |
CCJ |
CCK |
CCD |
CAD |
CFT |
|
初始表面电阻率(SR)(milliohms)﹡ |
CHO-TP-57*** |
﹤2 |
﹤2 |
﹤2 |
﹤2 |
N/A |
N/A |
﹤100 |
|
初始通过电阻率(TR)(milliohms)﹡ |
CHO-TP-57*** |
﹤3 |
﹤3 |
﹤35 |
﹤2 |
﹤15**** |
﹤100**** |
﹤100 |
|
初始撕裂强度oz./inch[ppi](N/m)﹡﹡ |
ASTM D1000 |
44.8 [2.8] (490) |
44.8 [2.8] (490) |
51.2 [3.2] (560) |
46.4 [2.9] (508) |
48 [3] (525) |
70.4 [4.4] (710) |
44.8 [2.8] (490) |
|
初始Taber磨损表面电阻率(SR)(milliohms) |
CHO-TP-57*** |
﹤6 |
﹤3 |
﹤6 |
﹤9 |
N/A |
N/A |
﹤100 |
|
热老化185℉(85℃)/168小时 (SR)(milliohms)﹡ (TR)(milliohms)﹡ 撕裂 oz./inch[ppi](N/m)﹡﹡ |
CHO-TP-57*** CHO-TP-57*** ASTM D1000 |
﹤10 ﹤16 57.6 [3.6] (630) |
﹤2 ﹤3 62.4 [3.9] (683) |
﹤20 ﹤22 76.8 [8] (840) |
﹤2 ﹤2 67.2 [4.2] (735) |
N/A ﹤7**** 73.6 [4.6] (805) |
N/A ﹤60**** 78.4 [4.8] (840) |
﹤100 ﹤150 59.2 [3.7] (648) |
|
热老化250℉(121℃)/168小时(SR)(milliohms)﹡ (TR)(milliohms)﹡ 撕裂 oz./inch[ppi](N/m)﹡﹡ |
CHO-TP-57*** CHO-TP-57*** ASTM D1000 |
﹤10 ﹤16 57.6 [3.6] (630) |
﹤3 ﹤3 59.2 [3.7] (648) |
﹤20 ﹤23 75.2 [4.7] (823) |
﹤2 ﹤2 51.2 [3.2] (560) |
N/A ﹤3**** 70.4 [4.4] (770) |
N/A ﹤10**** 84.8 [5.3] (928) |
﹤100 ﹤150 43.2 [2.7] (473) |
|
热老化相对温度95％/185℉(85℃) (SR)(milliohms)﹡ (TR)(milliohms)﹡ 撕裂 oz./inch[ppi](N/m)﹡﹡ |
CHO-TP-57*** CHO-TP-57*** ASTM D1000 |
N/A N/A N/A |
N/A N/A N/A |
N/A N/A N/A |
﹤2 ﹤2 78.4 [4.9] (858) |
N/A﹤115**** 78.4 [4.9] (858) |
N/A ﹤150**** 84.8 [5.3] (928) |
﹤100 ﹤150 46.4 [2.9] (508) |
|
盐雾腐蚀/小时 (SR)(milliohms)﹡ (TR)(milliohms)﹡ 撕裂 oz./inch[ppi](N/m)﹡﹡ |
CHO-TP-57*** CHO-TP-57*** ASTM D1000 |
N/A N/A N/A |
N/A N/A N/A |
N/A N/A N/A |
﹤2 ﹤2 76.8 [4.8] (840) |
N/A﹤275**** 62.4 [3.9] (683) |
N/A﹤600**** 80 [5] (875) |
﹤100 ﹤1000 33.6 [2.1] (368) |
|
Taber磨损500克重，CS-10轮500周 |
CHO-TP-57*** |
﹤3 |
﹤5 |
﹤2 |
﹤6 |
N/A |
N/A |
﹤175 |